1.The structure of brazed tips tools should be tough enough.

    Enough toughness shall be guaranteed by the maximum allowable sizes of the tips and by using a rather strong steel grade and heat treatment.

    2.Cemented carbide tips should be strongly fixed securely.

    The cemented carbide tips should have a secure fixation and it is guaranteed by the flutes of the tool holders and the quality in welding,so the flutes of the tools holders must be selected based on the shapes and the geometrical parameters of the tips.

    Before welding of the tips to the tool holders,a check must be done on the tips And the tool holders.

    An initial chesk must be done to ensure that there is no serious bending on the support surface of the tips.There shall be no serious carbulization on the welding surface of the tips and at the same time the contaminants on the surface of the tips and in the flutes of the tools holders must be eliminated to ensure the quality of a secure welding.

    3.There are requirements for the welding materials.

    In order to endure the toughness of the welding,a suitablewelding material must be selected.During the welding,good wettability and flowability must be guaranteed and the air bulbs must be got ridden of in order to ensure the sufficient contact of the welding material and the surface of the tips to be welded  leaving nothing to be welded.

    4.There are requirements for flux in the welding process.

    It is recommended that industrial borax is to be used.Before the use of the borax,it should be dewatered in a drying oven and then milled and sieved to get rid of the foreign objects.

    During the welding of cemented carbide tips of fine grain size with high titanium and low cobalt content and long and thin cemented carbide tips it will be recommended that compensation shims of a thickness of 0.2-0.5mm or similar shims with holes of 1-2mm in order to reduce the stress in the welding process.

    As cemented carbide tips are rather brittle and are most sensitive to the formation of cracks,excessive heating or rapid cooling must be prevented in the gringding of the tools and at the same time,gringding wheels with an appropriate grain size and hardness must be selected and a proper grinding technique to avoid cracks in the grinding of the edges of the tips and not to affect the lifetime of the tools.

    When the tools are installed,the length of the tips outstretching the tools must be as less as possiible,as otherwise the vibration of the tools will occur thus damaging the cemented carbide tips.

    When the tools come to a normal bluntness,they must be reground.The edges and the radius of the edges must be ground with oilstones after the tools are ground to increase the lifetime and reliability of the tools.